Note: This product is not to be used for windshield repair.
CARBON FILLED ELECTRICALLY CONDUCTIVE EPOXY
AA-CARB 61LP is an epoxy adhesive and coating formulation based on conductive carbon. This product's chemical formulation allows for micro-thin application and eliminted any air pockets or bubbling between thinly bonded substrates.
AA-CARB 61LP is recommended for electronic bonding and sealing applications that require both fine electrical and mechanical properties.
AA-CARB 61LP cures at room temperature or can be accelerated with mild heat to form a tenacious bond between similar and dissimilar substrates.
|Cure Type||Heat cure or Room temperature|
|Benefits||Continuity of conductivity
Wide operating temperature range
|Mix Ratio by weight||100:12 / Resin:Hardener|
|Substrates||Aluminum, copper, magnesium, steel, bronze, nickel, ceramic, glass, phenolic, G-10 epoxy glass boards|
|Operating Temperature||-50 to 170 °C|
|Typical Applications||Electronic bonding and sealing applications that require both fine electrical and mechanical properties.|
|Shelf Life||6 Months|
|Compressive Strength, psi||13,000|
|Specific Gravity, mixed||1.35 g/cc|
|Pot Life||3 Hours|
|15 minutes||@ 100°C|
|1 hour||@ 60°C|
|24 hours||@ 25°C|
|Volume Resistivity||ohm • cm: < 40|
|Tensile Strength, psi||8,500|
|Shrinkage Linear||0.003 in/in|
|Hardness, Shore D||85|
For safe handling information on this product, consult the Material Safety Data Sheet, (MSDS).
HOW TO USE:
1) Carefully clean and dry all surfaces to be bonded.
2) Apply AA-CARB 61 completely mixed adhesive to the prepared surfaces, and gently press these surfaces together. Contact pressure is adequate for strong, reliable bonds; however, maintain contact until adhesive is completely cured.
3) Some separation of components is common during shipping and storage. For this reason, it is recommended that the contents of the shipping container be thoroughly mixed prior to use.
4) Some ingredients in this formulation provided may crystallize when subjected to low temperature storage. A gentle warming cycle of 52°C for 30 minutes prior to mixing components may be necessary. Crystallized epoxy components do not react as well as liquid components and should be re-dissolved prior to use for best results.
This epoxy can be supplied in various different packages.